LG Chemical LUPOY SC1004L PC, High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY SC1004L PC, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC, General Purpose, High Flow, High Impact, Chemical ResistanceApplication: Mobile Phone HousingInformation provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 57.9 MPa @Thickness 3.20 mm |
8390 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 130 % @Thickness 3.20 mm |
130 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.11 GPa @Thickness 3.20 mm |
306 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 3.92 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
>= 7.35 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| >= 6.37 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 11.9 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C @Thickness >=0.700 mm |
176 °F @Thickness >=0.0276 in |
|
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness >=0.700 mm |
176 °F @Thickness >=0.0276 in |
|
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness >=0.700 mm |
176 °F @Thickness >=0.0276 in |
|
| Flammability, UL94 | HB @Thickness >=0.700 mm |
HB @Thickness >=0.0276 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 275 - 290 °C | 527 - 554 °F | Injection Molding |
| Middle Barrel Temperature | 285 - 305 °C | 545 - 581 °F | Injection Molding |
| Front Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Nozzle Temperature | 285 - 305 °C | 545 - 581 °F | Injection Molding |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Overview of materials for Styrenic TPE (Unverified Data**)
- Lanxess Durethan® AKV 35 H2.0 901510 Nylon 66, 35% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66 (Asia Pacific)
- CP-Polymer-Technik Wellamid® 6600 CF10 HWCP 10% Carbon Fiber Nylon 66, Heat Stabilized, Dry
- Diamond Polymers DIAMALOY PC 1008 Impact Modified Polycarbonate
- Fainplast Compounds PH 50/AM-UV Flexible PVC, Transparent Extrusion
- RheTech Products HP501-01 High Performance Polypropylene Copolymer, Non-UV Stabilized, Black
- BASF Ultradur® B 4300 G4 FC 20% Glass Filled PBT
- Bulk Molding Compounds BMC T70 Automotive Grade Molding compound
Copyright © lookpolymers.com All Rights Reserved