- LG Chemical LUPOY GP5100 PC/ABS+GF10%
LG Chemical LUPOY GP5100 PC/ABS+GF10%
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP5100 PC/ABS+GF10%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS+GF10%, General Purpose, GF ReinforcedApplication: Electrical Appliance Housing, Automotive I/PCAS: 103598-77-2, 9003-56-9 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 - 1.20 g/cc | 1.16 - 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 6.0 % @Thickness 3.20 mm |
6.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 4.81 GPa @Thickness 3.20 mm |
697 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.981 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 1.84 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Front Barrel Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 85.0 - 95.0 °C | 185 - 203 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.0200 - 0.0600 MPa | 2.90 - 8.70 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® MQ 74 High Density Polyethylene - Injection Molding
- Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced
- DuPont Elvax® 40L-08 Low Smoke Non-Halogen Jacket Formulation (discontinued **)
- Ineos ABS Lustran® 786 ABS, Extrusion Grade
- SABIC Innovative Plastics Noryl PX7446 PPE+PS
- SABIC Innovative Plastics NORYL WCP921 PPE-TPE
- Daikin POLYFLON MG-2060 PTFE 30% Graphite Filled Molding Powder
- Aclo Accutech Polypropylene Copolymer CP0436C10L Calcium Reinforced
- Akzo Nobel Trigonox® EHP-C75 Polymerization Initiator
Copyright © lookpolymers.com All Rights Reserved