LG Chemical LUPOY GP5008BFH PC/ABS, Flame Retardance

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GP5008BFH PC/ABS, Flame Retardance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, Flame Retardance, High Flow, Heat Resistant, High Impact Application: E&E (Housing)Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 260 °C
22 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D785
Tensile Strength, Yield 54.9 MPa

@Thickness 3.20 mm
7970 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 80 %

@Thickness 3.20 mm
80 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 89.2 MPa

@Thickness 3.20 mm
12900 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 2.40 GPa

@Thickness 3.20 mm
348 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched 5.39 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
10.1 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 123 °C

@Thickness 6.40 mm
253 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 85.0 °C

@Thickness >=0.820 mm
185 °F

@Thickness >=0.0323 in
85.0 °C

@Thickness >=1.50 mm
185 °F

@Thickness >=0.0591 in
85.0 °C

@Thickness >=3.00 mm
185 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=0.820 mm
149 °F

@Thickness >=0.0323 in
65.0 °C

@Thickness >=1.50 mm
149 °F

@Thickness >=0.0591 in
65.0 °C

@Thickness >=3.00 mm
149 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 70.0 °C

@Thickness >=0.820 mm
158 °F

@Thickness >=0.0323 in
70.0 °C

@Thickness >=1.50 mm
158 °F

@Thickness >=0.0591 in
70.0 °C

@Thickness >=3.00 mm
158 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
V-0

@Thickness >=0.118 in
5VB

@Thickness >=3.00 mm
5VB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
Dielectric Strength 38.0 kV/mm
965 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=0.820 mm
7.0 - 15 sec

@Thickness >=0.0323 in
7.0 - 15 sec

@Thickness >=1.50 mm
7.0 - 15 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=3.00 mm
30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 0.820 mm
30 - 60 arcs

@Thickness 0.0323 in
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Middle Barrel Temperature 235 - 255 °C
455 - 491 °F
Injection Molding
Front Barrel Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Nozzle Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Melt Temperature 235 - 265 °C
455 - 509 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.00200 - 0.00600 MPa
0.290 - 0.870 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding