LG Chemical LUPOY GP2200 PC+GF20%, Heat Resistance
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP2200 PC+GF20%, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC+GF20%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 5.0 % @Thickness 3.20 mm |
5.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 157 MPa @Thickness 3.20 mm |
22800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 5.39 GPa @Thickness 3.20 mm |
782 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.981 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 1.84 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| Flammability, UL94 | V-2 @Thickness >=1.50 mm |
V-2 @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 300 °C | 518 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Nozzle Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nylene® Vexel™ B50U , High Flow, Un-reinforced PBT
- Ineos ABS Lustran® H802
- H.C. Starck Amperit® 705.1 Fused Chromium Oxide 96.0 % (Cr2O3)
- Styron Pulse® 979 PC/ABS
- ExxonMobil 446 Mobilmet 440 Series
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- ExxonMobil Vistalon™ 3702 Ethylene Propylene Diene Terpolymer Rubber
- Dow C705-44NA Polypropylene Impact Copolymer Resin
- E-Polymers EFLEX® S5090 Extrusion
- RheTech Products HP522-357 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, JA6A Black
Copyright © lookpolymers.com All Rights Reserved