Borealis Daplen™ EE109AE TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE109AE TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EE109AE is a 20% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE109AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE109AE has been developed especially for bumpers, body side molding, and body panels.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Borealis Method
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 230 °C
13 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Elongation at Break 70 %
70 %
At 50 mm/min; ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
At 1 mm/min; ISO 527-2
Flexural Modulus 1.50 GPa
218 ksi
At 2 mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eA
0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
33.3 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Shrinkage 0.100 %

@Temperature 90.0 °C,
Time 7200 sec
0.100 %

@Temperature 194 °F,
Time 2.00 hour
Post Shrinkage; Borealis Method
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F