Toyobo T-422-02R Nylon, Mineral-Reinforced
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-422-02R Nylon, Mineral-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: High heat distortion and good toughness, high flowInformation provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.67 % | 0.67 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.00 mm |
0.0040 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0045 cm/cm @Thickness 3.00 mm |
0.0045 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Modulus of Elasticity | 7.30 GPa | 1060 ksi | ASTM D638 |
| Flexural Yield Strength | 133 MPa | 19300 psi | ASTM D790 |
| Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17 wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 29.0 kV/mm @Thickness 2.00 mm |
737 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 123 sec | 123 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Nye Lubricants 885FG (FG) Synthetic Oil
- DuPont™ Surlyn® 9970 Ionomer Resin, Zinc (discontinued **)
- Lanxess Durethan® BKV 30 000000 Nylon 6, 30% Glass Fiber
- Saint-Gobain Vitreosil® CFQ/TSC Optical Fused Quartz
- Total HDPE B5845 High Density Polyethylene - Blow Molding Resin
- Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction, Heat Treated
- ChevronTexaco Bright-Cut® AXH Metal Working Fluid
- DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 50 Gauge
- Arkema Group Rilsan® AZM 43 G9 T6LD Nylon 12, 43% Glass Fiber Filled (Dry)
- Beijing Chemical Industry KAIFA® 304-G30 PBT Resin
Copyright © lookpolymers.com All Rights Reserved