PolyOne Geon™ Vinyl Rigid Extrusion L7007 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L7007 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Geon L7007 is recommended for whites and light pastel colors only.Geon L7007 is a higher gloss version of L7005.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 43.2 MPa | 6270 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.85 GPa | 413 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| Izod Impact, Notched | 5.90 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
11.1 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 73.4 J/cm @Temperature 23.0 °C |
0.138 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 178 J/cm @Temperature 23.0 °C |
0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
165 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C @Thickness 3.18 mm |
160 °F @Thickness 0.125 in |
Compression Molded, Annealed at 50 deg.C; ASTM D648 |
| 74.4 °C @Thickness 3.18 mm |
166 °F @Thickness 0.125 in |
Compression Molded, Annealed at 60 deg.C; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | Good Impact Resistance | |
| Good Weather Resistance | ||
| Medium Gloss | ||
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 1-42434-33 | ASTM D4216 |
| 15354 | ASTM D1784 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications | |
| Profiles | ||
| Windows & Doors |
Users viewing this material also viewed the following:
- LG Chemical Butyl Acrylate
- Gwent Electronic Materials P2121112P5 Ammonia Plasma Modified Graphene Nanoplatelets
- Multibase C6-265 DI-CUP R Dow-Corning Class VI Elastomer
- Styrolution PS 476L HIPS
- A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66
- Dow Corning TM-4012 DISPERSION
- ExxonMobil Exact™ 9361 Ethylene-based Plastomer Resin
- E-Polymers TEKAMID® TB120G60W , 62% Glass Fiber Reinforced PA6, DAM