LG Chemical LUPOY ER5001RFA PC/ABS, Halogen Free, Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical LUPOY ER5001RFA PC/ABS, Halogen Free, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EPEATApplication: IT&OA (Notebook PC housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm <br>@Thickness 3.20 mm |
0.0040 - 0.0060 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min <br>@Load 2.16 kg,<br> Temperature 260 °C |
25 g/10 min <br>@Load 4.76 lb,<br> Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.8 MPa <br>@Thickness 3.20 mm |
8820 psi <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 97.1 MPa <br>@Thickness 3.20 mm |
14100 psi <br>@Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa <br>@Thickness 3.20 mm |
370 ksi <br>@Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
>= 9.18 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C <br>@Thickness 6.40 mm |
201 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 <br>@Thickness >=1.20 mm |
V-0 <br>@Thickness >=0.0472 in |
|
| V-0 <br>@Thickness >=1.50 mm |
V-0 <br>@Thickness >=0.0591 in |
||
| V-0 <br>@Thickness >=3.00 mm |
V-0 <br>@Thickness >=0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 225 - 240 °C | 437 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 255 °C | 464 - 491 °F | Injection Molding |
| Front Barrel Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.0200 - 0.0600 MPa | 2.90 - 8.70 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products T20P100-01UV 20% Talc Reinforced Polypropylene, UV Stabilized, General Purpose Black
- S&E Specialty Polymers G-04-036ESD PVC
- Custom Resins Vexel™ E20GF30 , 30% Glass Reinforced PET (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66
- Teknor Apex APEX® 90-P513A-85-NT Polyvinyl Chloride+PUR
- Teknor Apex APEX® 65006 Polyvinyl Chloride, Flexible
- Solvay RHODOLINE® 697 Surfactant
- DSM Arnitel® PB582-H Polyether Ester Elastomer (European and Asian Grade)
- ExxonMobil Exceed™ 1018KA Metallocene Polyethylene Resin (Asia Pacific Grade)
- Diamond Polymers SAN 300 Styrene Acrylonitrile, Transparent Engineering Thermoplastic
Copyright © lookpolymers.com All Rights Reserved