LG Chemical LUPOL TE-5108 Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Flow

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer LG Chemical
Trade Name LUPOL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOL TE-5108 Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive exterior parts.Information Provided by LG Chem
Physical Properties Metric English Comments
Specific Gravity 0.970 g/cc
0.970 g/cc
ASTM D792
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 20.0 MPa
2900 psi
ASTM D638
Elongation at Break 500 %
500 %
ASTM D638
Flexural Strength 26.0 MPa
3770 psi
ASTM D790
Flexural Modulus 1.27 GPa
184 ksi
ASTM D790
Izod Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 200 - 220 °C
392 - 428 °F
Middle Barrel Temperature 200 - 230 °C
392 - 446 °F
Front Barrel Temperature 210 - 230 °C
410 - 446 °F
Nozzle Temperature 210 - 240 °C
410 - 464 °F
Melt Temperature 210 - 240 °C
410 - 464 °F
Mold Temperature 40.0 - 90.0 °C
104 - 194 °F
Drying Temperature 70.0 - 90.0 °C
158 - 194 °F
Dry Time 2 - 3 hour
2 - 3 hour
Injection Pressure 29.4 - 118 MPa
4260 - 17100 psi
First
78.45 - 98.07 MPa
11380 - 14220 psi
Second
Back Pressure 0.490 - 3.92 MPa
71.1 - 569 psi
Screw Speed 40 - 60 rpm
40 - 60 rpm