LATI Latiohm 63-08 PD02 G/25 PA6, 25% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer LATI
Trade Name Latiohm
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 63-08 PD02 G/25 PA6, 25% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dissipative product based on Polyamide 6 (PA6), impact modified. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Linear Mold Shrinkage, Flow 0.0045 - 0.0060 cm/cm
0.0045 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0090 cm/cm
0.0065 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 6.10 GPa
885 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Deflection Temperature at 1.8 MPa (264 psi) 145 °C
293 °F
Vicat Softening Point 145 °C

@Load 5.00 kg
293 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Electrical Properties Metric English Comments
Surface Resistance 1.00e+9 ohm
1.00e+9 ohm
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa