Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 20.0 MPa | >= 2900 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIPOLEN® (Polyethylene) UHMW-PE 1000 PE 1000: Polyethylene with very high molecular weight (UHMW - PE 1000; Ultra High Molecular Weight Polyethylene). Polyethylenes with molecular weight higher than 3 million gr/mol. POLIPOLEN® PE (P.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® ESD 5500 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5500 is a static dissipative thermoplastic compound based on polypropylene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 5500 can be injectio.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
Quadrant EPP Cestlite™ ASTL Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
NOVA Chemicals Sclair® 51-35BP HDPE Extrusion Resin Features: Medium molecular weight, excellent ESCR, excellent toughness, good processability, good chemical resistance.Applications: Extrusion on to metal pipes to produce a corrosion resistant coati.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir RK Polystyrene
(discontinued **) UL94 V-0, flame retarded, high impact polystyrene. This grade is suitable for injection moulding. It combines high mechanical strength, heat resistance and good processability.
Designation: Thermopl.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
NOVA Chemicals Sclair® 2717 HDPE Injection Molding Resin
(discontinued **) Features: Super high flow, good balance of toughness and stiffness, low odor, permits container weight reduction.Applications: Thin walled food containers.Data provided by the manufacturer. |
|||
Tensile Strength, Yield | 20.0 - 76.0 MPa | 2900 - 11000 psi | Average value: 39.5 MPa Grade Count:34 |
Overview of materials for Nylon 12, Extrusion/Tubing Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Extrusion/Tubing Grade". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ASTM D638 |
ICO Polymers ICORENEâ„¢ 155-4060 LMDPE Rotational Molding Resin Description: ICORENE 155-4060 is a linear medium density polyethylene developed for use in rotational molding. It has a great combination of stiffness and toughness in a resin that is easy processi.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 60°C for 500 hrs with 95% RH |
Fujipoly Industries Sarcon® 85GSR Thin-Film GSR Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
LG Chemical LUPOL TE-5108 Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Flow LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive exterior parts.Information Provided by LG Chem |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D412 |
Teknor Apex Flexalloy® 3501-75-NT Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MW, Ethylene Oxide SterilizableForms-PelletsProcessing-Extrusion, Injection MoldingAppe.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Techmer ES HiFill FR® HIPS 1000 FR-E Availability: North AmericaForms: PelletsFeatures: Flame RetardantRoHS Compliance: RoHS CompliantInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | Compound; ASTM D638 |
Borealis Borcell™ HE1345 High Density Polyethylene Compound for Cellular Insulation of Telephone Singles Borcell HE1345 is a high molecular weight, high-density polyethylene (HDPE) insulation compound containing an industry approved non plate-out chemical blowing agent and contains the required levels .. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled) DescriptionPolyfort® FPP 1434 is a 25% coupled mica copolymer polypropyleneInformation provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
Polyram RamShine PS580 High Impact Polystyrene, Flame Retardant Flame retardant V-0, high impact polystyrene for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Total PS CPDS 815 High Flow, Non-Deca Polystyrene Total Petrochemicals Polystyrene 815 is a high heat resistant, high impact Polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensional stab.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ FPP 1434 Couple Mica In Copolymer Polypropylene (25% Mineral Filled) DescriptionPolyfort® FPP 1434 is a 25% coupled mica copolymer polypropyleneInformation provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
Trelleborg R499 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | Type IV; 50 mm per min crosshead speed; ASTM D638 |
Chevron Phillips Marlex® K307 MDPE Hexene Copolymer Extrusion grade hexene copolymerCharacteristics: good processability, excellent melt strength, broad fusion range, outstanding stress crack resistance, meets the requirements of GRI-GM13. Meets A.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527-2 |
ExxonMobil Exxtral™ BMV 208 Performance Polyolefin Product Description: Polyolefin injection molding compound with very high flow, high stiffness, good low temperature impact resistance, and excellent processability for automotive exterior trim appl.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D-638 |
Axiall 11890 Wire & Cable Flexible PVC High gloss, flame retardant jacketing compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Multibase Multi-Pro® 4007 XGS Polypropylene Mineral, 40% by weight.Features:Gloss, HighScratch ResistantForms:PelletsProcessing Methods:Injection MoldingUses: FurnitureAppliancesInformation provided by Multibase |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Petromont 7001 Medium Density Polyethylene Resin Petromont HDPE 7001 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is designed to be readily processed by flat die extrusi.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | DIN 53.504 |
Lubrizol Advanced Materials PEARLBOND® 151 Linear Thermoplastic Polyurethane
(discontinued **) PEARLBOND® 125/H is polycaprolactone-based thermoplastic polyurethane, supplied in form of colourless or slightly yellowish, translucid pellets, combining a low hardness with excellent low-temperat.. |
|||
Tensile Strength, Yield | 20.0 - 142 MPa @Temperature -40.0 - 121 °C |
2900 - 20600 psi @Temperature -40.0 - 250 °F |
Average value: 74.0 MPa Grade Count:16 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | At 50 mm/min; ISO 527-2 |
Borealis Daplen™ KSX65T20 Polypropylene Compound 20% Mineral Filled Daplen KSX65T20 is a 20% mineral filled grade intended for injection molding. Daplen KSX65T20 has been developed especially for the car industry, to be used in interior parts. Daplen KSX65T20 offe.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Reliance Industries Relene B31101 Polyethylene Steel pipe coating base High Density Polyethylene resin. Characteristics:broad molecular weight distribution, good melting strength, excellent toughness/ESCR, and good cut through/abrasion resistanc.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | 2 in/min, injection molded, type 1 specimen; ASTM D638 |
Phillips Sumika Marlex® ABF-110 Reactor Thermoplastic Polyolefin, Cold Temperature Impact Resistant
(disconti Applications: Automotive fascias and claddingsConsumer productsTotes and binsInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011. .. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON MS000IL PP LNP* STAT-KON* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food c.. |
|||
Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
Kostat BK-STAT P048BK PP Sheet BK-STAT Sheets are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanliness .. |