- LG Chemical LUMID HI5001AH PA6/PO, High Melt Strength, High Barrier property, CaCl2 Resistance
LG Chemical LUMID HI5001AH PA6/PO, High Melt Strength, High Barrier property, CaCl2 Resistance
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI5001AH PA6/PO, High Melt Strength, High Barrier property, CaCl2 Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6/PO, High Melt Strength, High Barrier property, CaCl2 ResistanceApplication: Automotive (Fuel System Tube)CAS No. 25038-54-4, 9010-79-1 and 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Temperature 23.0 °C, Time 86400 sec |
0.50 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | 3.0 g/10 min @Load 12.5 kg, Temperature 260 °C |
3.0 g/10 min @Load 27.6 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 320 % @Thickness 3.20 mm |
320 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 48.1 MPa @Thickness 6.40 mm |
6970 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 1.32 GPa @Thickness 6.40 mm |
192 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 2.55 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
4.78 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1010G10 HB Polycarbonate, 10% Fiberglass Reinforced
- Permabond UV649 UV-curable Adhesive
- MetalTek C86300 High Tensile Manganese Bronze
- ITW Devcon Flexane® Rubber Repair / Castable Urethane Belt Repair Kit, Black
- Momentive Performance Materials FQE207U Heat Cured Fluorosilicone Rubber
- SABIC Innovative Plastics LNP LUBRILOY D2000P PC
- Seals Eastern 5053 Ethylene-Propylene Rubber
- DuPont Performance Polymers Delrin® 900P NC010 Acetal (POM) (Unverified Data**)
- Barlog Plastics KEBATRON C1065X1 PPS, cross-linked, 65% glass fiber / mineral reinforced
Copyright © lookpolymers.com All Rights Reserved