LG Chemical LUMID GP3300A(W) PA6+MF30%, General Purpose

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP3300A(W) PA6+MF30%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6+MF30%, General PurposeApplication: Automotive (Battery Pack Housing)Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D792
Water Absorption 1.1 %
1.1 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 78.5 MPa

@Thickness 3.20 mm
 11400 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 4.0 %

@Thickness 3.20 mm
 4.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 123 MPa

@Thickness 3.20 mm
 17800 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 5.39 GPa

@Thickness 3.20 mm
 782 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 0.918 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 34.0 µm/m-°C
18.9 µin/in-°F
ASTM D696
Melting Point 220 °C
428 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 160 °C

@Thickness 6.40 mm
 320 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
Flammability, UL94 HB

@Thickness >=0.750 mm
 HB

@Thickness >=0.0295 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 22.0 kV/mm

@Thickness 1.00 mm
 559 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 185 sec
185 sec
ASTM D495
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=0.750 mm
 7.0 - 15 sec

@Thickness >=0.0295 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 270 °C
482 - 518 °F
Injection Molding
Middle Barrel Temperature 255 - 275 °C
491 - 527 °F
Injection Molding
Front Barrel Temperature 255 - 275 °C
491 - 527 °F
Injection Molding
Nozzle Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding