Solvay Specialty Polymers Ixef® 2060 Polyarylamide (PARA)  (discontinued **)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 2060 Polyarylamide (PARA)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 2060 is a 55% reinforced, general purpose polyarylamide compound. This compound exhibits improved vibration resistance, low warpage, and excellent surface finish. This grade has excellent properties in the transverse direction. - Black: Ixef 2060/9008 - Custom ColorableInjection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Injection Pressure: rapid Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 2060 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be between 265°C to 275°C (477-495°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 290°C (500°F to 554°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C to 140°C (248°F and 284°F). Molding at a lower temperature will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ISO 1183
Filler Content 55 %
55 %
Glass Fiber
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.2 %
1.2 %
65% RH
Linear Mold Shrinkage, Flow 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
Linear Mold Shrinkage, Transverse 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
Weldline; ISO 527-2
180 MPa
26100 psi
ISO 527-2
Elongation at Break 1.5 %
1.5 %
ISO 527-2
Tensile Modulus 19.0 GPa
2760 ksi
ISO 527-2
Flexural Strength 270 MPa
39200 psi
ISO 178
Flexural Modulus 18.0 GPa
2610 ksi
ISO 178
Charpy Impact Unnotched 2.70 J/cm²
12.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.440 J/cm²
2.09 ft-lb/in²
ISO 179
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 247 - 257 °C
477 - 495 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C

@Time 1800 - 5400 sec
248 °F

@Time 0.500 - 1.50 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
High Flow
High Strength
Low Moisture Absorption
Low Warpage
Outstanding Surface Finish
Ultra High Stiffness
Forms Pellets
Processing Method Injection Molding
RoHS Compliance RoHS Compliant