LG Chemical LUCON TR1000 PMMA+CNT
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON TR1000 PMMA+CNT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PMMA+CNT, Transparency, Permanent Antistatic, Low OutgassingApplication: Wafer Carrier Cover, Pellicle TrayCAS No. 9010-94-0 and 25053-09-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm |
7970 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 85.3 MPa @Thickness 3.20 mm |
12400 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 3.20 mm |
313 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.451 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 0.845 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % | 10 % | ASTM D1003 |
| Transmission, Visible | 75 % | 75 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.00e+12 ohm | 2.00e+12 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.490 - 0.981 MPa | 71.1 - 142 psi | Injection Molding |
| Screw Speed | <= 80 rpm | <= 80 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/HS/BK Polyamide 66, with glass fiber and PTFE, heat stabilized
- LATI Latigea B01 L/07 Bio-Polymer
- Sylvin Technologies 9077-90 Natural PVC for Injection Molding
- Samsung Cheil Industries Starex® NH-1904 HIPS, Unreinforced FR
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- Covestro Bayfol® DF-A 1-2 900296 Polycarbonate + ABS
- ChevronTexaco Meropa® 3200
- Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66
- SABIC Innovative Plastics Lexan® HFD4471 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved