Tipco Tipcolene® FPW 10 PPC - 10% Wollastonite Reinforced Polypropylene Copolymer, High Impact Strength
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcolene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcolene® FPW 10 PPC - 10% Wollastonite Reinforced Polypropylene Copolymer, High Impact Strength.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Wollastonite Reinforced PP CopolymerApplications: Automotive & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.5 MPa | 4130 psi | ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D638 |
| Flexural Yield Strength | 38.0 MPa | 5510 psi | ASTM D790 |
| Flexural Modulus | 1.74 GPa | 252 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | >= 7.00 kJ/m² | >= 3.33 ft-lb/in² | ASTM D638 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 124 PC
- SABIC Innovative Plastics Lexan® 950A PC (Asia Pacific)
- Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes
- Taiwan Sheen Soon Sheenthane® AH-650 TPU for Hotmelt Adhesive
- Saint-Gobain COHRlastic® 200A Silicone Sponge/Aggressive Acrylic Adhesive Pressure Sensitive Tape
- CP-Polymer-Technik Wellamid® 6000 MF 30 HWCP 30% Milled Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Radici Heraflex® P 55D 11 I HF 330 Modified Polypropylene
Copyright © lookpolymers.com All Rights Reserved