Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer LG Chemical
Trade Name LUCON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON CP6067 PC+CNT+CF.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC+CNT+CF, Electrostatic Dissipation, High Strength, High Flow & Good ProcessabilityApplication: Wafer Carrier Box, Conveyor belt bearing blockCAS No. 103598-77-2, 7440-44-0 and 7782-42-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0040 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 60 g/10 min

@Load 2.16 kg,
Temperature 300 °C
60 g/10 min

@Load 4.76 lb,
Temperature 572 °F
ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength, Yield 98.1 MPa

@Thickness 3.20 mm
14200 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break >= 7.0 %

@Thickness 3.20 mm
>= 7.0 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 147 MPa

@Thickness 3.20 mm
21300 psi

@Thickness 0.126 in
15mm/min; ASTM D790
Flexural Modulus 6.28 GPa

@Thickness 3.20 mm
910 ksi

@Thickness 0.126 in
15mm/min; ASTM D790
Izod Impact, Notched 0.324 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
0.606 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 135 °C

@Thickness 6.40 mm
275 °F

@Thickness 0.252 in
ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 1e+05 - 1.00e+6 ohm
1e+05 - 1.00e+6 ohm
IEC 60093
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 300 °C
536 - 572 °F
Injection Molding
Middle Barrel Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Front Barrel Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Nozzle Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Melt Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 5.00 - 7.00 hour
5.00 - 7.00 hour
Injection Molding
Back Pressure 0.000 - 1.96 MPa
0.000 - 284 psi
Injection Molding
Screw Speed 40 - 60 rpm
40 - 60 rpm
Injection Molding