SABIC Innovative Plastics Lexan® 105 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® 105 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose low flow Polycarbonate powder gradeThis data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ASTM D 570 |
| 0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | >= 70 % | >= 70 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 9.07 J/cm @Temperature 23.0 °C |
17.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 64.0 J @Temperature 23.0 °C |
47.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 154 °C | 309 °F | Rate B/50; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP CCF30 Homopolymer Polypropylene Calcium Carbonate Filled
- PolyOne Lubri-Tech™ SF-25GF/13T-2S Polyphenylene Sulfide (PPS), Glass Filled, PTFE/Silicone Lubricated (disco
- Materion BrushCAST® 20CT Fine Grain Casting Alloy (As Cast & Aged)
- Solvay GEROPON® SC/213 Surfactant
- SABIC Innovative Plastics Noryl PKN4717 PPE+PS (Asia Pacific)
- Lubrizol Stat-Rite® X-5111 Static Control Polypropylene
- Plastics Group Polifil® RP-PP Polypropylene, Black
- CLAL-MSX NICLAFOR® 1000 TH4 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy
- Formosa Plastics Formolene® 5140L Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved