Rogers Corporation Bisco™ BF-1000 Cellular Silicone Foam

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Foam
Manufacturer	Rogers Corporation
Trade Name	Bisco™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Rogers Corporation Bisco™ BF-1000 Cellular Silicone Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Soft, low compression set silicone foam often specified to meet safely-conscious requirements. UL recognized for flame retardance.Applications: Low closure-force gaskets and seals, Vibration and shock isolation in electronic components and aircraft, Flame retardant, low toxicity insulation in aircraft and trains, Automotive airbag cushion seals, Industrial machinery insulationNo UV degradation per SAE J-1960. Ozone effect rating is 0 (no cracks) per ASTM D-1171. No staining per ASTM D-925(A). Passes AMS-3568 corrosion resistance. Passes SMP-800-C & BSS toxic gas emission rating. Passes hot flex at 230°C (446°F) per ASTM D-573.General BISCO™ silicone information: BISCO™ Cellular Silicones are used as sealing cushioning, vibration isolation, insulation, and thermal management gaskets. Their resistance to environmental extremes, mechanical resilience, and safety features lead to their use in transportation equipment, communications and electrical enclosures, electronic products and components, industrial machinery, and appliances.Data provided by Rogers Corporation.

Physical Properties	Metric	English	Comments
Density	0.192 g/cc	0.00694 lb/in³	ASTM D3574
Water Absorption	3.5 %	3.5 %	ASTM D471

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	0.241 MPa	35.0 psi	ASTM D412
Elongation at Break	100 %	100 %	ASTM D412
Compressive Yield Strength	0.0140 MPa	2.03 psi	at 25% deflection; ASTM D1056
Compression Set	<= 1.0 % @Temperature 70.0 °C	<= 1.0 % @Temperature 158 °F	ASTM D1056
	<= 5.0 % @Temperature 100 °C	<= 5.0 % @Temperature 212 °F	ASTM D1056

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0600 W/m-K	0.416 BTU-in/hr-ft²-°F	ASTM C158
Maximum Service Temperature, Air	200 °C	392 °F	Recommended use; SAE J-2236
	250 °C	482 °F	Intermittent; Rogers internal test
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F	Recommended use; SAE J-2236
Brittleness Temperature	-55.0 °C	-67.0 °F	Low temp embrittlement; ASTM D746(B)
Flammability, UL94	V-0	V-0	Listed (may vary with thickness, color, density)
Flame Spread Index	<= 25	<= 25	I<sub>S</sub>; ASTM E162
Smoke Density	<= 20 min	<= 20 min	D<sub>X</sub> at 1.5 minutes; ASTM E662
	<= 50 min	<= 50 min	D<sub>X</sub> at 4 minutes; ASTM E662
Oxygen Index	34 %	34 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D257
Dielectric Constant	1.34	1.34
Dielectric Strength	3.50 kV/mm	88.9 kV/in	ASTM D150
Arc Resistance	90 sec	90 sec	Dry; ASTM D495