Eurotec® Tecomid® NAX0 GR60 NL PA6.6, 60% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NAX0 GR60 NL PA6.6, 60% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.00 % @Temperature 23.0 °C |
1.00 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 235 MPa | 34100 psi | ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 |
| Vicat Softening Point | 255 °C @Load 5.10 kg |
491 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 3460 Amorphous Polyalphaolefin (APAO)
- SABIC Innovative Plastics LNP LUBRICOMP RP002 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON MD000A PP
- Saint-Gobain Norton® Fluorglas® Chemfilm® DF1400 Non-Conductive PTFE Tape
- Teknor Apex APEX® 1002 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL EM6100 PPE+PS
- A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
- UBE V115 Polyethylene
- Wieland 1023 Wilaform Gold
- Arlon 912-10C16.4FR-P0 0.012" (0.305 mm) Self-Fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved