LG Chemical KEYFLEX BT 3055D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 3055D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, Functional, Fast Molding, Medium ModulusApplication: Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 54 | 54 | ASTM D2240 |
| Tensile Strength at Break | 22.6 MPa @Thickness 2.00 mm |
3280 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 350 % @Thickness 2.00 mm |
350 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.265 GPa @Thickness 6.40 mm |
38.4 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
3.67 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Zone 1 | 220 - 250 °C | 428 - 482 °F | Extrusion Molding |
| Zone 2 | 220 - 240 °C | 428 - 464 °F | Extrusion Molding |
| Zone 3 | 225 - 245 °C | 437 - 473 °F | Extrusion Molding |
| Zone 4 | 225 - 245 °C | 437 - 473 °F | Extrusion Molding |
| Adapter Temperature | 225 - 245 °C | 437 - 473 °F | Extrusion Molding |
| Die Temperature | 220 - 255 °C | 428 - 491 °F | Extrusion Molding |
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| 220 - 250 °C | 428 - 482 °F | Extrusion Molding | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1013HL Nylon 6/6 (Cond)
- Polimeri Europa Eraclene® MM 74 High Density Polyethylene - Injection Molding
- IRPC Polimaxx Polene 330PC Styrene Acrylonitrile
- Solvay TECHNYL® C 548B V15 Black PA6, 15% glass filled, DRY
- Solvay Chemicals Trifluoroacetic acid isopropyl ester
- Samsung Cheil Industries Starex® TX-0520T TRABS, Unreinforced
- Master Bond Supreme 3HTND-2GT One Part, Toughened, Fast Curing Glob Top Adhesive
- ExxonMobil Teresstic 77
- Advanced Ceramics ALC 1081 (C-786) Alumina
Copyright © lookpolymers.com All Rights Reserved