A. Schulman FORMION™ FI 395 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 395 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.018 - 0.026 cm/cm @Thickness 3.20 mm |
0.018 - 0.026 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | at max load; ISO 527 |
| Tensile Strength, Yield | 2.80 MPa @Strain 100 % |
406 psi @Strain 100 % |
ISO 527 |
| 3.60 MPa @Strain 300 % |
522 psi @Strain 300 % |
ISO 527 | |
| Elongation at Break | 1100 % | 1100 % | ISO 527 |
| Flexural Modulus | 0.0600 GPa | 8.70 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180 |
Users viewing this material also viewed the following:
- MV Labs FE870 (NH4)3Fe(C2O4)3·3H2O Ammonium iron(III) oxalate
- Kazanorgsintez 107-22 Composition of Low Density Polyethylene, Crack-Proof
- Mateck Glass (BK7 Schott or analogous)
- SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific)
- Techmer ES HiFill® HDPE UV
- STAR Thermoplastic Alloys & Rubbers StarGrip GP 30-1000 TPE
- Chevron Phillips MarFlex® 9607 HDPE Cast Film Resin
- 3M 6145 White Light Duty Reinforced Water Activated Tape
- Asahi Kasei Thermofil P-40TC-2767 40% Talc Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved