LG Chemical ALPHALAC SG970NSU HIPS

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Grade, Glass Filled
Manufacturer LG Chemical
Trade Name ALPHALAC
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical ALPHALAC SG970NSU HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, General Purpose, Good Processability, High gloss, antistatic and UV stabilizedApplication: Air Conditioner Panel, Washer CoverCAS No. 9003-55-8Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0040 - 0.0080 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 6.5 g/10 min
<br>@Load 5.00 kg,<br> Temperature 200 °C
 6.5 g/10 min
<br>@Load 11.0 lb,<br> Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
Tensile Strength, Yield 35.3 MPa
<br>@Thickness 3.20 mm
 5120 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 50 %
<br>@Thickness 3.20 mm
 50 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Yield >= 5.0 %
<br>@Thickness 3.20 mm
 >= 5.0 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 53.9 MPa
<br>@Thickness 3.20 mm
 7820 psi
<br>@Thickness 0.126 in
 15mm/min; ASTM D790
Flexural Modulus 2.55 GPa
<br>@Thickness 3.20 mm
 370 ksi
<br>@Thickness 0.126 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.392 J/cm
<br>@Thickness 6.50 mm,<br> Temperature -30.0 °C
 0.735 ft-lb/in
<br>@Thickness 0.256 in,<br> Temperature -22.0 °F
 ASTM D256
0.490 J/cm
<br>@Thickness 3.20 mm,<br> Temperature -30.0 °C
 0.918 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature -22.0 °F
 ASTM D256
0.981 J/cm
<br>@Thickness 6.50 mm,<br> Temperature 23.0 °C
 1.84 ft-lb/in
<br>@Thickness 0.256 in,<br> Temperature 73.4 °F
 ASTM D256
1.18 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 2.20 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
<br>@Thickness 6.40 mm
 199 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
<br>@Thickness 6.40 mm
 181 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 91.0 °C
<br>@Load 5.00 kg
 196 °F
<br>@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C
<br>@Thickness >=1.50 mm
 122 °F
<br>@Thickness >=0.0591 in
50.0 °C
<br>@Thickness >=3.00 mm
 122 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C
<br>@Thickness >=1.50 mm
 122 °F
<br>@Thickness >=0.0591 in
50.0 °C
<br>@Thickness >=3.00 mm
 122 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C
<br>@Thickness >=1.50 mm
 122 °F
<br>@Thickness >=0.0591 in
50.0 °C
<br>@Thickness >=3.00 mm
 122 °F
<br>@Thickness >=0.118 in
Flammability, UL94 HB
<br>@Thickness >=1.50 mm
 HB
<br>@Thickness >=0.0591 in
HB
<br>@Thickness >=2.50 mm
 HB
<br>@Thickness >=0.0984 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Hot Wire Ignition, HWI 15 - 30 sec
<br>@Thickness >=3.00 mm
 15 - 30 sec
<br>@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs
<br>@Thickness 3.00 mm
 >= 120 arcs
<br>@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Melt Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding