Lehmann & Voss LUVOCOM® 1/CF/20 Polyamide 66, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1/CF/20 Polyamide 66, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 210 MPa | 30500 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 3.5 % | 3.5 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 315 MPa | 45700 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | flatwise; ISO 179 1fU |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 1eA |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | |
| Coefficient of Friction, Static | 0.17 | 0.17 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 1.00 W/m-K | 6.94 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 160 °C | 320 °F | short term | |
| Vicat Softening Point | 255 °C | 491 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE1810T PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics Valox® 7062HP PBT (Asia Pacific)
- Teknor Apex Telcar® TL-1424A Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66
- Dow Corning MOLYKOTE® 1122 CHAIN AND OPEN GEAR GREASE
- Dow Corning DM2 Demulsifier
- Americas Styrenics Styron® 612 Polystyrene (discontinued **)
- ExxonMobil 524 Mobil SHC 500 Series
Copyright © lookpolymers.com All Rights Reserved