Permabond MH199 Anaerobic Gasketmaker

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond MH199 Anaerobic Gasketmaker.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Permabond® MH199 is an anaerobic material designed for making “formed in situ” gaskets between metal surfaces. It is capable of replacing a wide range of conventional gaskets, thereby offering potential for reduced stock holdings. By allowing surface to surface contact, load transmission can be improved. As the product does not shrink, creep or relax after curing, no bolt re-tightening is required. It has excellent chemical and high temperature resistance or up to 200°C. Features & Benefits: Replaces all sizes of formed gaskets Does not creep or shrink Good high pressure resistance High temperature resistance No shimming effect Information provided by Permabond.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Uncured
Viscosity	75000 cP @Temperature 25.0 °C	75000 cP @Temperature 77.0 °F	at 20 rpm vibration
	225000 cP @Temperature 25.0 °C	225000 cP @Temperature 77.0 °F	at 2 rpm vibration

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	8.00 MPa	1160 psi	steel collar and pin shear; ISO 10123

Thermal Properties	Metric	English
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F
Thermal Conductivity	0.190 W/m-K	1.32 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	199 °C	390 °F
Minimum Service Temperature, Air	-53.9 °C	-65.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	11.0 kV/mm	279 kV/in

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 23.0 °C	0.500 hour @Temperature 73.4 °F	M10 steel, handling strength
	60.0 min @Temperature 23.0 °C	1.00 hour @Temperature 73.4 °F	Zinc, handling strength
	180 min @Temperature 23.0 °C	3.00 hour @Temperature 73.4 °F	Aluminum, handling strength
	180 - 360 min @Temperature 23.0 °C	3.00 - 6.00 hour @Temperature 73.4 °F	M10 steel, working strength
	360 - 1440 min @Temperature 23.0 °C	6.00 - 24.0 hour @Temperature 73.4 °F	Zinc, working strength
	1440 min @Temperature 23.0 °C	24.0 hour @Temperature 73.4 °F	M10 steel, full strength

Descriptive Properties	Value	Comments
Appearance	Red	Uncured
Maximum Gap Fill (mm)	0.5
Strength Retention	20% at 250°C	Relative to 0°C
	70% at 200°C	Relative to 0°C
	85% at 150°C	Relative to 0°C
	93% at 100°C	Relative to 0°C
	98% at 50°C	Relative to 0°C
Torque Strength (N m)	12	M10 steel, prevail
	20	M10 steel, break
UV Fluorescence	Yes	Uncured