LATI Latishield 66-10A H2 CETG/400 PA66, Steel/Glass Fiber Reinforced, Mineral Filled, Heat Stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Stainless Steel Filled; EMI Grade
Manufacturer	LATI
Trade Name	Latishield
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latishield 66-10A H2 CETG/400 PA66, Steel/Glass Fiber Reinforced, Mineral Filled, Heat Stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.57 g/cc	0.0567 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0050 - 0.0065 cm/cm	0.0050 - 0.0065 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.010 cm/cm	0.0070 - 0.010 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	100 MPa	14500 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	11.0 GPa	1600 ksi
Charpy Impact Unnotched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Charpy Impact, Notched	0.400 J/cmÂ²	1.90 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	260 Â°C	500 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	240 Â°C	464 Â°F
Vicat Softening Point	245 Â°C @Load 5.00 kg	473 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	200 ohm-cm	200 ohm-cm
Surface Resistance	20 ohm	20 ohm

Processing Properties	Metric	English
Melt Temperature	275 - 300 Â°C	527 - 572 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	90.0 - 100 Â°C	194 - 212 Â°F

Descriptive Properties	Value	Comments
Electromagnetic reflection	90 dB
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: