Adell AT-37 Nylon 66, 35% Glass Reinforced; Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell AT-37 Nylon 66, 35% Glass Reinforced; Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 221 MPa | 32100 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Perstorp Compounds 136 Urea-Formaldehyde w/ cellulose filler
- Lehmann & Voss LUVOCOM® 50/TF/15/BK-1 Polycarbonate, with PTFE, easy flowing
- Michelman® Michem® Emulsion 93135M Nonionic polyethylene emulsion
- ELASTO UK Dryflex® 8013-101 Flame Retardant TPE for Extrusion, Black
- DuPont Performance Polymers Crastin® S600F20 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- AK Steel ASTM A 607 Class 2 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- Alliance Polymers Viprene™ P60A-22U-BLK Thermoplastic Vulcanizate Elastomer
- 3M Scotch-Weld™ Hi-Strength Postforming 94 CA Spray Adhesive
- Axiall 01561 Plenum Flexible PVC
- Fiberfil® J-68/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
Copyright © lookpolymers.com All Rights Reserved