Covestro Makrolon® FR 7067 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized
Manufacturer Covestro
Trade Name Makrolon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® FR 7067 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Medium viscosity, easy release• UV stabilizedAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 75.0 MPa
10900 psi
50 mm/min; ISO 527-1,-2
Elongation at Break 100 %
100 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527-1,-2
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179-1eU
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75-1,-2
Vicat Softening Point 123 °C

@Load 5.10 kg
253 °F

@Load 11.2 lb
50°C/h; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL-94 5V
Glow Wire Test 960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 3.00 mm
2.0 %

@Thickness 0.118 in
ISO 14782
Transmission, Visible 88 %

@Thickness 3.00 mm
88 %

@Thickness 0.118 in
ISO 13468-2
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 200 mm/sec
7.87 in/sec
ISO 294