LATI Latamid 6 H2 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 6 H2 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa @Temperature 150 °C |
10200 psi @Temperature 302 °F |
|
| 80.0 MPa @Temperature 120 °C |
11600 psi @Temperature 248 °F |
||
| 95.0 MPa @Temperature 90.0 °C |
13800 psi @Temperature 194 °F |
||
| 125 MPa @Temperature 60.0 °C |
18100 psi @Temperature 140 °F |
||
| 160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 4.0 % @Temperature 60.0 °C |
4.0 % @Temperature 140 °F |
||
| 5.3 % @Temperature 90.0 °C |
5.3 % @Temperature 194 °F |
||
| 5.8 % @Temperature 120 °C |
5.8 % @Temperature 248 °F |
||
| 6.5 % @Temperature 150 °C |
6.5 % @Temperature 302 °F |
||
| Tensile Modulus | 3.10 GPa @Temperature 150 °C |
450 ksi @Temperature 302 °F |
|
| 3.80 GPa @Temperature 120 °C |
551 ksi @Temperature 248 °F |
||
| 4.70 GPa @Temperature 90.0 °C |
682 ksi @Temperature 194 °F |
||
| 7.10 GPa @Temperature 60.0 °C |
1030 ksi @Temperature 140 °F |
||
| 8.80 GPa @Temperature 23.0 °C |
1280 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® X11 ABS
- Permabond HH040 Anaerobic Retainer
- Lucent Polymers LPB-130 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- STAR Thermoplastic Alloys & Rubbers StarMediflex P 7070-1000 TPE
- Westlake Plastics Propylux® HS2 Polypropylene for Medical Applications, Heat Stabilized
- Formosa Plastics Formolene® E602 Pipe HDPE
- Trelleborg Emerson & Cuming Stycast® E-151-8 One-Component Epoxy Flexible Encapsulant
- Dow DOWLEX™ 2025G Linear Low Density Polyethylene
- C.O.I.M. LARIPUR® LPR5225 Special Adipate Ester Polyurethane
- Aclo Accutech Polypropylene Homopolymer HP0339T20L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved