Lubrizol Isoplast® 101LGF40BLK Engineering Thermoplastic Polyurethane Resin
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Isoplast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Isoplast® 101LGF40BLK Engineering Thermoplastic Polyurethane Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | ASTM D638 |
| Tensile Strength, Yield | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 9.60 GPa | 1390 ksi | ASTM D790 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.99 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| 3.20 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
5.99 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Annealed; ASTM D648 |
| 93.0 °C | 199 °F | Unannealed; ASTM D648 | |
| Vicat Softening Point | 186 °C | 367 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 65.0 - 90.0 °C | 149 - 194 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- Eastman 812A Polyethylene (discontinued **)
- KKPC Kuhmo HFH 403 Flame Retarded HIPS
- SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER
- Teknor Apex Flexalloy® 9800-40 Polyvinyl Chloride Elastomer
- ExxonMobil 100 Special Mobiltemp SHC Series
- Crucible Steel REX® TMO High Speed Steel, AISI M1
- Epoxy Technology EPO-TEK® 320-3 Optically Opaque Epoxy
- Azoty Tarnow™ TARNOFORM 500 HI4 POM
- Carlisle 201HD Carbon-Carbon Composite
- Axiall 22882 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved