Kingfa JH950-402 Flame Retardant PC/ABS Alloy

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Kingfa Sci. & Tech. Co.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kingfa JH950-402 Flame Retardant PC/ABS Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features:UL V-0 @ 3.2mmExcellent balance propertiesHigh heat resistanceGood normal/low temperature impact strengthGood surfaceApplications:Small household appliance cabinetControllerSocketShell of ammeterInformation Provided by Kingfa Sci. & Tech. Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc @Temperature 23.0 Â°C	1.12 g/cc @Temperature 73.4 Â°F	ASTM D792
Water Absorption	0.15 % @Temperature 23.0 Â°C, Time 86400 sec	0.15 % @Temperature 73.4 Â°F, Time 24.0 hour	ASTM D570
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm @Temperature 23.0 Â°C	0.0040 - 0.0060 in/in @Temperature 73.4 Â°F	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	114	114	ASTM D785
Tensile Strength at Break	50.0 MPa	7250 psi	50mm/min; ASTM D638
Elongation at Break	>= 30 %	>= 30 %	50mm/min; ASTM D638
Flexural Strength	85.0 MPa	12300 psi	2mm/min; ASTM D790
Flexural Modulus	2.30 GPa	334 ksi	2mm/min; ASTM D790
Izod Impact, Notched	>= 2.50 J/cm @Thickness 3.20 mm, Temperature -30.0 Â°C	>= 4.68 ft-lb/in @Thickness 0.126 in, Temperature -22.0 Â°F	ASTM D256
	>= 3.40 J/cm @Thickness 3.20 mm, Temperature 23.0 Â°C	>= 6.37 ft-lb/in @Thickness 0.126 in, Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	80.0 Âµm/m-Â°C	44.4 Âµin/in-Â°F	ASTM D696
Hot Ball Pressure Test	118 - 122 Â°C @Thickness 2.00 mm	244 - 252 Â°F @Thickness 0.0787 in	IEC695-10-2
Deflection Temperature at 0.46 MPa (66 psi)	120 Â°C @Thickness 6.40 mm	248 Â°F @Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	105 Â°C @Thickness 6.40 mm	221 Â°F @Thickness 0.252 in	ASTM D648
Flammability, UL94	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	ASTM D257
Dielectric Strength	28.0 kV/mm	711 kV/in	1.6mm; ASTM D149

Processing Properties	Metric	English	Comments
Processing Temperature	<= 260 Â°C	<= 500 Â°F
Rear Barrel Temperature	210 - 230 Â°C	410 - 446 Â°F	Start Point: 215Â°C
Middle Barrel Temperature	220 - 230 Â°C	428 - 446 Â°F	Start Point: 225Â°C
Front Barrel Temperature	220 - 240 Â°C	428 - 464 Â°F	Start Point: 235Â°C
Melt Temperature	220 - 240 Â°C	428 - 464 Â°F	Start Point: 230Â°C
Mold Temperature	60.0 - 100 Â°C	140 - 212 Â°F	Start Point: 70Â°C
Drying Temperature	90.0 - 100 Â°C @Time 10800 - 21600 sec	194 - 212 Â°F @Time 3.00 - 6.00 hour	Pre-dry
Back Pressure	0.000 - 1.00 MPa	0.000 - 145 psi

Descriptive Properties	Value	Comments
Hot Wire Test (Â°C)	850	IEC695-2-12, 1.6mm
Injection Speed	60-90%