SABIC Innovative Plastics NORYL WCP921A PPE-TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL WCP921A PPE-TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connectors. UL 94 V-0 performance with good processability. GreenScreen Approved.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 173000 sec |
0.10 % @Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| 12 g/10 min @Load 5.00 kg, Temperature 210 °C |
12 g/10 min @Load 11.0 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | 30S reading; ASTM D2240 |
| Tensile Strength at Break | 9.00 MPa | 1310 psi | Type I, 50 mm/min; ASTM D638 |
| 9.00 MPa | 1310 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| 120 % | 120 % | 50 mm/min; ISO 527 | |
| Flexural Modulus | 0.110 GPa | 16.0 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
| 0.110 GPa | 16.0 ksi | 12.5 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
UL 94 |
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Glow Wire Test | 775 °C | 1430 °F | IEC 60695-2-13 |
| 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+15 ohm-cm | 4.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 65-7712/GY PP-copolymer, with carbon fiber and glass fiber, electrically conducting
- Mallard Creek Polymers Rovene® 4301 Styrene-Butadiene Emulsion
- Techmer ES HiFill FR® PA6/6 GB30 FR 30% Glass Bead Filled
- Master Bond UV10 One Component UV Curable Adhesive System
- DSM Akulon® K125/A PA6
- Covestro Makrolon® 3156 Polycarbonate
- Bapolene® 142F Polyethylene Film Grade
- Advanced Ceramics ACL 2089 Cordierite
- Plastcom SLOVALEN PH 91 GF 15 Polypropylene Homopolymer, 15% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved