BASF Ultraform® W2320 U035 LEV POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® W2320 U035 LEV POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM, UV-stabilized, very free-flowing, rapidly solidifying grade for injection molding, with reduced emission potential.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm | 0.023 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.023 cm/cm | 0.023 in/in | ISO 2577 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 190 °C |
35 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 135 MPa @Load 36.5 kg, Time 30.0 sec |
19600 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 25 % | 25 % | ISO 527-2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-2 |
| Modulus of Elasticity | 2.45 GPa | 355 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 19.0 J/cm² @Temperature -30.0 °C |
90.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 20.0 J/cm² @Temperature 23.0 °C |
95.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 1.50 µm/m-°C @Temperature 23.0 - 55.0 °C |
0.833 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 166 °C | 331 °F | DIN 53765 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-2 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Decomposition Temperature | >= 240 °C | >= 464 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 190 °C | 374 °F | Feed zone |
| Zone 2 | 195 °C | 383 °F | Compression |
| Zone 3 | 195 °C | 383 °F | Metering-zone |
| Zone 4 | 195 °C | 383 °F | Nozzle |
| Melt Temperature | 195 °C | 383 °F | Optimal |
| 190 - 220 °C | 374 - 428 °F | Injection-molding | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding |
| 90.0 °C | 194 °F | Optimal | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 3 hour | 3 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 320 - 340°C | ASTM D1929 |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs PT450 (NH4)2PtCl4 Ammonium tetrachloroplatinate(II)
- Northstar Polymers MPN-055 Polyether Prepolymer
- Ravago Manufacturing Americas Hysun™ A3525 ASA+PC
- Plansee DENSIMET® D180 Tungsten-Nickel-Iron Alloy
- RheTech Products G20P252-01 20% Glass Fiber Reinforced Polypropylene Copolymer, Black
- Lanxess Durethan® BC 40 SR2 000000 Nylon 6
- SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Europe-Africa-Middle East)
- TIMCAL TIMREX® SFG44 Primary Synthetic Graphite
- Dow 722 Linear Low Density Polyethylene (LDPE)
Copyright © lookpolymers.com All Rights Reserved