Kingfa H-12 Modified ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer	Kingfa Sci. & Tech. Co.
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Kingfa H-12 Modified ABS.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Features:UL94 HB @ 1.6-3.0mmHigh toughnessHeat resistanceApplications:Automobile exterior trimAutomobile interior trimPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc <br>@Temperature 23.0 Â°C	1.04 g/cc <br>@Temperature 73.4 Â°F	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm <br>@Temperature 23.0 Â°C	0.0040 - 0.0070 in/in <br>@Temperature 73.4 Â°F	ASTM D955
Melt Flow	2.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 Â°C	2.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 Â°F	ASTM D1238
	25 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 Â°C	25 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ASTM D785
Tensile Strength at Break	44.0 MPa	6380 psi	50mm/min; ASTM D638
Elongation at Break	25 %	25 %	50mm/min; ASTM D638
Flexural Strength	64.0 MPa	9280 psi	2mm/min; ASTM D790
Flexural Modulus	2.20 GPa	319 ksi	2mm/min; ASTM D790
Izod Impact, Notched	2.61 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 Â°C	4.89 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 Â°F	ASTM D256
	2.89 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 Â°C	5.41 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	97.0 Â°C <br>@Thickness 6.40 mm	207 Â°F <br>@Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	88.0 Â°C <br>@Thickness 6.40 mm	190 Â°F <br>@Thickness 0.252 in	ASTM D648
Vicat Softening Point	96.0 Â°C <br>@Load 5.00 kg	205 Â°F <br>@Load 11.0 lb	50Â°C/min; ASTM D1525
	104 Â°C <br>@Load 1.00 kg	219 Â°F <br>@Load 2.20 lb	120Â°C/min; ASTM D1525
Flammability, UL94	HB <br>@Thickness 1.50 mm	HB <br>@Thickness 0.0591 in
	HB <br>@Thickness 3.00 mm	HB <br>@Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Strength	23.0 kV/mm	584 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Processing Temperature	<= 250 Â°C	<= 482 Â°F
Rear Barrel Temperature	180 - 205 Â°C	356 - 401 Â°F	Start Point: 190Â°C
Middle Barrel Temperature	205 - 230 Â°C	401 - 446 Â°F	Start Point: 215Â°C
Front Barrel Temperature	215 - 240 Â°C	419 - 464 Â°F	Start Point: 225Â°C
Melt Temperature	220 - 245 Â°C	428 - 473 Â°F	Start Point: 230Â°C
Mold Temperature	30.0 - 60.0 Â°C	86.0 - 140 Â°F	Start Point: 50Â°C
Drying Temperature	80.0 - 90.0 Â°C <br>@Time 7200 - 14400 sec	176 - 194 Â°F <br>@Time 2.00 - 4.00 hour	Pre-dry
Back Pressure	0.000 - 1.00 MPa	0.000 - 145 psi

Descriptive Properties	Value	Comments
Injection Speed	Slow to Moderate