Ineos ABS Lustran® 288 ABS, Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® 288 ABS, Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® ABS 288 is a very high-flow injection molding grade of ABS (acrylonitrile butadiene styrene) with good impact strength and high gloss. It is intended for use in a wide range of applications, particularly in thin-walled components for telecommunications, office equipment, consumer and other office products.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM-D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM-D955
Melt Flow 30 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 30 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM-D1238, ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 38.0 MPa
5510 psi
ISO 527
Tensile Modulus 2.80 GPa
406 ksi
ISO 527
Flexural Strength 66.0 MPa
9570 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Thickness 4.00 mm,
Temperature -30.0 °C
 6.19 ft-lb/in²

@Thickness 0.157 in,
Temperature -22.0 °F
 ISO 180
24.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
 11.4 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
 ISO 180
Impact Test 9.00 J

@Temperature -30.0 °C
 6.64 ft-lb

@Temperature -22.0 °F
 Instrumented Impact; Total Energy; ASTM-D3763
40.0 J

@Temperature 23.0 °C
 29.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact; Total Energy; ASTM-D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C

@Thickness 4.00 mm
 185 °F

@Thickness 0.157 in
 Unannealed; ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C

@Thickness 4.00 mm
 169 °F

@Thickness 0.157 in
 Unannealed; ISO 75
Vicat Softening Point 94.0 °C

@Load 5.00 kg
 201 °F

@Load 11.0 lb
 50°C/hour; ISO 306
104 °C

@Load 1.00 kg
 219 °F

@Load 2.20 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Optical Properties Metric English Comments
Gloss 95 %
95 %
Angle 60°; ASTM-D523
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 255 °C
464 - 491 °F
Injection Molding
Front Barrel Temperature 245 - 260 °C
473 - 500 °F
Injection Molding
Nozzle Temperature 245 - 260 °C
473 - 500 °F
Injection Molding
Melt Temperature 245 - 265 °C
473 - 509 °F
Injection Molding
Mold Temperature 45.0 - 65.0 °C
113 - 149 °F
Injection Molding
Drying Temperature 71.0 - 77.0 °C

@Time 14400 sec
 160 - 171 °F

@Time 4.00 hour
82.0 - 88.0 °C

@Time 7200 sec
 180 - 190 °F

@Time 2.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Dew Point <= -29.0 °C
<= -20.2 °F
inlet air
Injection Pressure 68.9 - 110 MPa
10000 - 16000 psi
Injection Molding
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Injection Molding
Clamp Pressure 30.8 - 61.6 MPa
4470 - 8930 psi
Injection Molding
Cushion <= 0.635 cm
<= 0.250 in
Injection Molding
Descriptive Properties Value Comments
Hold Pressure 50-75% of Injection Pressure, Injection Molding
Injection Speed High
Injection Molding
Screw Compression Ratio 2.5:1
Injection Molding
Screw Length-to-Diameter Ratio >= 20:1
Injection Molding
Screw Speed Moderate, Injection Molding
Shot Weight-to-Machine Capacity Ratio 0.5-0.75
Injection Molding