Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 38.0 - 42.0 MPa | 5510 - 6090 psi | ASTM D638 |
Prodways PLASTCure Rigid 10 500 3D Printing Polymer Superior thermo-mechanical properties.Suitable for the manufacture of parts that require thermal stability, extreme accuracy and quick turnaround. Exceptional for parts that are designed for wind tu.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTWE480 ASA (Asia Pacific) Anti-scratch Geloy grade with excellent weatherability, high flow, and good surface quality. XTWE480 is available in various colours.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | >= 38.0 MPa | >= 5510 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 353B General Purpose Polystyrene Grade 535 is a high heat crystal polystyrene designed for injection molding, extrusion and blow molding. It is used for electronic packaging, extruded light diffusers and office accessories.Informa.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RH 211/W Rigid PVC, Antishock Extrusion Various antishock profiles |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RH 212/W Rigid PVC, Antishock Extrusion Outdoor antishock profiles |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RI 52 Rigid PVC, Injection Molding Fittings for building trade |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RKS 212/W Rigid PVC, Antishock Extrusion Lead Free Outdoor antishock profiles |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copolymer LNP* Lubricomp* KX99792 is a compound based on Acetal Copolymer resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the .. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY A3000TXJ ABS LNP* STAT-LOY* A3000TXJ is a product based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS (Asia Pacific) LNP* Stat-loy* AF306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. Added features of this material include: Antistat. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp C7410 PC+ABS (Asia Pacific) LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PVX524 PPE PREVEX* PVX524 resin is a high flow, non FR grade, 100 C HDT |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-2 |
Tisan TISAKRIL® Flame Retardant (V0) ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Toyobo PELPRENE™ P150B Polyester TPE Features: Polyester TPEInformation provided by Toyobo. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Toyobo PELPRENE™ P150B-05 Polyester TPE, Non-smell, Non-deposit Features: Polyester TPE, Non-smell, Non-depositInformation provided by Toyobo. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Toyobo PELPRENE™ S2002 Polyester TPE, Ultra Heat-resistant Features: Polyester TPE, Ultra Heat-resistantInformation provided by Toyobo. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Eastman Eastar DN001HF Copolyester Applications:DisplaysPersonal care and CosmeticsProduct Description: Eastar Copolyester DN001HF has excellent flow characteristics while maintaining superior mechanical properties. It is easy to p.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-1/-2 |
DSM Arnitel® EL740 74 Shore D, Injection Grade Copolyester Elastomer (North America) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-1/-2 |
DSM Arnitel® EL740 Polyether Ester Elastomer (European and Asian Grade) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50mm/min; ISO 527-2 |
Denka MALECCA K-700 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-777D ABS - High Heat Super High Heat |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds ARC 30 Rigid PVC, Atoxic for General Purpose Bottles very high antishock |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
Braskem GM8250T HDPE High Density Extrusion Polyethylene GM8250T is a high-density polyethylene specially developed for the manufacturing of corrugated pipes. It has high molar mass and shows excellent tenacity, high stiffness, good impact resistance, and.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
Braskem GM8260 HDPE Blow Molding Polyethylene Homopolymer HDPE GM8260 is a high-density polyethylene homopolymer that has high molecular weight and was developed for the blow molding segment of large volumes. Its applications include: drums for lubricant .. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
Braskem GP5550 HDPE High Density Extrusion Polyethylene GP5550 is a high-density polyethylene with high molar mass. It is produced with bimodal technology and shows excellent mechanical properties and high resistance to stress cracking. Its applications .. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM-D638 |
Braskem GP5550BK HDPE High Density Extrusion Polyethylene GP5550BK is a high-density polyethylene with high molar mass. It is produced with bimodal technology and shows excellent mechanical properties and high resistance to stress cracking. GP5550BK contai.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
BASF Ultramid® HFX 33 PA6 (Dry) Description: Ultramid HFX 33 is a polyamide specialty extrusion resin combining high flexibility, excellent burst performance and outstanding chemical resistance. It offers high melt strength and en.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RI 52/C Rigid PVC, Injection Molding Electric fittings |