- Idemitsu Kosan Xarec® WA 552 SPS, 30% Glass Filled
Idemitsu Kosan Xarec® WA 552 SPS, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® WA 552 SPS, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer, Glass Filled/Impact Modified. Used in Automotive and Industrial applications. NSF and medical approval ISO 10993
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | |
| Elongation at Break | 2.3 % | 2.3 % | |
| Tensile Modulus | 9.10 GPa | 1320 ksi | |
| Flexural Yield Strength | 185 MPa | 26800 psi | |
| Flexural Modulus | 8.90 GPa | 1290 ksi | |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C | 27.2 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec @Thickness 1.50 mm |
>= 120 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | ISO10993 | |
| NSF61 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK) (Unverified Data**)
- McDanel Advanced Ceramics MV-HR1 Mullite
- Solvay Specialty Polymers Diofan® A 297 Polyvinylidene Chloride (PVDC)
- Shin-Etsu Silicones KF-9009 Fluid
- EMS-Grivory Grivory® HT2V-3H LF PA*-GF30
- DuPont Teijin Films Melinex® ST339 Polyester Film, 700 Gauge
- DuPont Performance Polymers Hytrel® HTR8730 BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- Fainplast Compounds PM 95/7 Flexible PVC, Extrusion
- Carpenter Super Invar 32-5
- BASF Ultramid® HPN 9233G HS BK 102 33% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved