Idemitsu Kosan Xarec® EA 543 SPS, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® EA 543 SPS, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.020 % | 0.020 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | |
| Elongation at Break | 1.6 % | 1.6 % | |
| Tensile Modulus | 12.9 GPa | 1870 ksi | |
| Flexural Yield Strength | 200 MPa | 29000 psi | |
| Flexural Modulus | 13.1 GPa | 1900 ksi | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | |
| Charpy Impact Unnotched | 2.90 J/cm² | 13.8 ft-lb/in² | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 29.0 µm/m-°C | 16.1 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| UL RTI, Electrical | 125 °C | 257 °F | UL746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.5 | 3.5 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D145 |
| Dissipation Factor | 0.0030 | 0.0030 | IEC 60250 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec @Thickness 1.50 mm |
>= 120 sec @Thickness 0.0591 in |
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckshield®-F 100 OPI 0.0022" Diameter Wire, High Performance EMC Window
- IDI Composites M-207 Thermoset Polyester, Sheet
- LATI Latilub 87/28-17ST K/15 PC, 15% Carbon Fiber Reinforced, Silicone/PTFE Filled
- Techmer ES Statiblend® PA6/6 GF20 AS BK 20% Glass Filled
- Styron EMERGEâ„¢ 7600 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- Tipco Tipcolite® TPF 1512 Phenolic Resin having 680 cps Viscosity containing 68% Solids
- ChevronTexaco Transultex® D
- Braskem ML3601U LLDPE Rotomolding Polyethylene
- Ametek P409L/409CB P/M Stainless Steel, Sintered from 6.00 g/cc Green Density
- KKPC KOSYN KTR 402 Thermoplastic Elastomer (TPE)
Copyright © lookpolymers.com All Rights Reserved