Idemitsu Kosan Xarec® EA 537 SPS, 30% Glass Filled

Category Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber
Manufacturer Idemitsu Kosan Co., Ltd.
Trade Name Xarec®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Idemitsu Kosan Xarec® EA 537 SPS, 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crystalline Polymer, Glass Filled, Ignition Resistant, Impact Modified. Used in Electronic and Electrical applications
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Filler Content 30 %
30 %
Water Absorption 0.010 %
0.010 %
24 hrs., 50% RH
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 11.6 GPa
1680 ksi
Flexural Yield Strength 185 MPa
26800 psi
Flexural Modulus 10.9 GPa
1580 ksi
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
Izod Impact, Unnotched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
Charpy Impact Unnotched 3.20 J/cm²
15.2 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 8.33 µin/in-°F

@Temperature -22.0 - 86.0 °F
CTE, linear, Transverse to Flow 47.0 µm/m-°C
26.1 µin/in-°F
Deflection Temperature at 0.46 MPa (66 psi) 265 °C
509 °F
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
UL RTI, Electrical 125 °C
257 °F
UL746B
UL RTI, Mechanical with Impact 120 °C
248 °F
UL746B
UL RTI, Mechanical without Impact 120 °C
248 °F
UL746B
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 1.50 mm
 5VA

@Thickness 0.0591 in
5VA

@Thickness 2.30 mm
 5VA

@Thickness 0.0906 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Constant 3.2
3.2
Dielectric Strength 32.0 kV/mm
813 kV/in
ASTM D145
Dissipation Factor 0.0020
0.0020
IEC 60250
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec

@Thickness 1.50 mm
 30 - 60 sec

@Thickness 0.0591 in
 UL 746A
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL746A
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
130 - 155 °C
266 - 311 °F
For optimal surface finish
Descriptive Properties Value Comments
Comments ISO10993
Thin wall V0 & 5VA