- Eurotec® Tecomid® NB40 MF20 GR003 FY70 PA6, 20% mineral filled, flame retardant - halogen free (RoHS compliant), grey RAL 7035
Eurotec® Tecomid® NB40 MF20 GR003 FY70 PA6, 20% mineral filled, flame retardant - halogen free (RoHS compliant), grey RAL 7035
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NB40 MF20 GR003 FY70 PA6, 20% mineral filled, flame retardant - halogen free (RoHS compliant), grey RAL 7035.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.70 % @Temperature 23.0 °C |
1.70 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | [10 K/min], ISO 11357 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
||
| Glow Wire Test | 800 °C @Thickness 2.00 mm |
1470 °F @Thickness 0.0787 in |
GWIT; IEC 60695 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 250 °C | 446 - 482 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- MV Labs PR900 PrPO4 Praseodymium(III) phosphate
- Resinlab® CYNERGY CA6404 Adhesive
- SABIC Innovative Plastics Lexan® 3412R PC (Asia Pacific)
- Gromax BFG30-FU03B3 Nylon 6 32.9% Glass Filled (Dry)
- Menzolit Menzolit® BMC 3000 Unsaturated Polyester UP
- SABIC Innovative Plastics ULTEM 2110 PEI (Asia Pacific)
- DuPont Teijin Films Melinex® 377 Polyester Film, 92 Gauge
- Fainplast Compounds GS 7430 Flexible PVC, Injection Molding for Footwear
- DSM Akulon® S223-DK Nylon 66 (European Grade) (Dry)
- Parkway Products Thixomolded® AZ91D Magnesium
Copyright © lookpolymers.com All Rights Reserved