- Eurotec® Tecomid® NB30 GR15 BK005 FS90 PA6, 15% glass fiber reinforced, flame retardant - halogen & red phosphorus free, low smoke & toxic gas grade
Eurotec® Tecomid® NB30 GR15 BK005 FS90 PA6, 15% glass fiber reinforced, flame retardant - halogen & red phosphorus free, low smoke & toxic gas grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NB30 GR15 BK005 FS90 PA6, 15% glass fiber reinforced, flame retardant - halogen & red phosphorus free, low smoke & toxic gas grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.10 % @Temperature 23.0 °C |
1.10 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75 |
| Vicat Softening Point | 205 °C @Load 5.10 kg |
401 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| Glow Wire Test | 850 °C @Thickness 2.00 mm |
1560 °F @Thickness 0.0787 in |
GWIT; IEC 60695 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 250 °C | 446 - 482 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Nye Lubricants 880 (FG) Synthetic Oil
- Nitriflex SB-1011 Styrene Butadiene Copolymer
- SABIC Innovative Plastics Lexan® OQ4620 PC
- LG Chemical HIPS MI750L PS, Impact Modified
- Ecomass® 1080CO94 Copper Powder Filled Polyamide Alloy, Injection Molding
- Ensinger TECAPEI® made from Ultem® 1000 PEI
- Carborundum CarboTherm™ CTL30 Boron Nitride Powder
- BASF Ultramid® A3K Q601 PA66 (Dry)
- 3A Composites Core Materials AIREX® T90.150 Easy Processing Structural FST Foam
Copyright © lookpolymers.com All Rights Reserved