Samsung Cheil Industries Infino® HR-1008B PC/ABS, Unreinforced

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Samsung, Cheil Industries
Trade Name Infino®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Infino® HR-1008B PC/ABS, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC/ABS material that can be used for hand phone and car phoneInformation provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Melt Flow 60 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 60 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Tensile Strength at Break 61.8 MPa
8960 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 59.8 MPa
8680 psi
50 mm/min; ASTM D638
Elongation at Break 104 %
104 %
50 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
327 ksi
50 mm/min; ASTM D638
Flexural Strength 83.4 MPa
12100 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 2.65 J/cm

@Thickness 6.35 mm
 4.96 ft-lb/in

@Thickness 0.250 in
 ASTM D256
5.88 J/cm

@Thickness 3.17 mm
 11.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C

@Thickness 6.40 mm
 264 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 6.40 mm
 230 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 119 °C
246 °F
B/50; ISO R306
123 °C
253 °F
B/120; ISO R306
Flammability, UL94 HB

@Thickness 1.50 - 6.00 mm
 HB

@Thickness 0.0591 - 0.236 in