Eurostar Starflam PX06004 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PX06004 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX06004 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.20 % @Temperature 23.0 °C |
2.20 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 9.0 % @Temperature 23.0 °C |
9.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 5.6 % | >= 5.6 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.7 % | 3.7 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80x10x4; ISO 180/1U |
| Charpy Impact Unnotched | >= 10.0 J/cm² @Temperature 23.0 °C |
>= 47.6 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 10.0 J/cm² @Temperature -30.0 °C |
>= 47.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 200 °C | 392 °F | B/120; ISO 306 |
| 205 °C | 401 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 130 °C | 266 °F | |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | |
| UL RTI, Mechanical without Impact | 100 °C | 212 °F | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0078 @Frequency 50.0 - 60.0 Hz |
0.0078 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV-3766 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Chevron Phillips 4522 LDPE Shrink and Heavy Duty Packaging Film Resin (discontinued **)
- Braskem BI 818 LDPE Injection Molding Polyethylene (discontinued **)
- Garlock LEAK-GARDâ„¢ 3750 Compressed Aramid Fiber Gasketing
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- 3M 9500B Double Coated Tapes with Adhesive 350
- Arkema Group Lacovyl® PE 1801 H PVC
- BorsodChem ONGRONAT PA-28 MDI Isocyanate
- Fainplast Compounds RE 130 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved