- SABIC Innovative Plastics LNP Stat-kon ZX05043 PPE+PS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Stat-kon ZX05043 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon ZX05043 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* ZX05043 is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE, Carbon Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| Flexural Strength | 133 MPa | 19300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.6 GPa | 1830 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Rogers Corporation XT/duroid™ 8000 Thermoplastic Laminate, Circuit Material
- Quadrant EPP TIVAR® HPV UHMW-PE (ASTM Product Data Sheet)
- PolyOne Bergamid™ B650 Mi10 Polyamide 6 (Nylon 6)
- Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled
- LG Chemical XR440 ABS, Low Emission High Heat ABS
- Momentive Performance Materials BNC2 Boron Nitride (BN) Refractory Composite
- Henkel Frekote 700-NC Mold Release Agent
- SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved