- Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled
Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 127 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Flexural Modulus | 9.12 GPa | 1320 ksi | ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Quantum Composites QC-8700 63% Glass Fiber Reinforced Vinyl Ester SMC
- M Chemical GUARD DOGâ„¢ UV9 Light Stabilizer, Benzophenone Derivative
- Lucas-Milhaupt BRAZE 380
- Lanxess Durethan® C 38 FAM 000000 Copolyamide
- Washington Penn PPH2CF2 Polypropylene, 20% Calcium Carbonate Reinforced
- Polyram RamLloy PFS301G6 ASA/PBT Alloy, 30% Glass Fiber
- Chosun Refractories RSP-M Blast Furnace Runner Refractory
- DSM Stanyl® TS200F10 PA46-GF50
- H.C. Starck Amperit® 335.066 Nickel Self-fluxing Alloy HRC 60 (NiCrBSi)
Copyright © lookpolymers.com All Rights Reserved