Eurostar Starflam BFR460B1 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam BFR460B1 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam BFR460B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption at Saturation 4.0 %

@Temperature 23.0 °C
 4.0 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 9.00 GPa
1310 ksi
1 mm/min; ISO 527
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
9.00 kJ/m²

@Temperature -20.0 °C
 4.28 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 10.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 212 °C
414 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL RTI, Mechanical without Impact 65.0 °C
149 °F
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Glow Wire Test 800 °C

@Thickness 1.00 mm
 1470 °F

@Thickness 0.0394 in
 Ignitability; IEC 60695-2-13
825 °C

@Thickness 2.00 mm
 1520 °F

@Thickness 0.0787 in
 Ignitability; IEC 60695-2-13
875 °C

@Thickness 3.00 mm
 1610 °F

@Thickness 0.118 in
 Ignitability; IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 240 - 250 °C
464 - 482 °F
Zone 2 250 - 260 °C
482 - 500 °F
Zone 3 250 - 270 °C
482 - 518 °F
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C

@Time 14400 sec
 176 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %