PolyOne Stat-Tech™ PF-05CF/000 EM FR Flame Retardant Polysulfone - 5% Carbon Fiber  (discontinued **)

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Stat-Tech™ PF-05CF/000 EM FR Flame Retardant Polysulfone - 5% Carbon Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ASTM D792
Water Absorption 0.60 %
0.60 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm

@Thickness 3.17 mm
 0.0030 - 0.0040 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 MPa
13100 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Yield Strength 155 MPa
22500 psi
ASTM D790
Flexural Modulus 4.40 GPa
638 ksi
ASTM D790
Izod Impact, Notched 0.640 J/cm

@Thickness 6.35 mm
 1.20 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 179 °C
354 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 338 - 360 °C
640 - 680 °F
Stock
Mold Temperature 82.0 - 121 °C
180 - 250 °F
Drying Temperature 121 - 135 °C
250 - 275 °F