Addiplast Addilene H 442 M30 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 442 M30 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat resistance, detergent stabilizedInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Melt Flow | 14 g/10 min | 14 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | ISO 868 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO R 527 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R 527 |
| Elongation at Yield | 11 % | 11 % | ISO R 527 |
| Modulus of Elasticity | 3.20 GPa | 464 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/IeU |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | CEI 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Nye Lubricants 371B (RL) Synthetic Oil
- Permabond F201 Anaerobic Retainer
- Johnson Matthey Mattibraze 50N Silver Brazing Alloy for Tungsten Carbide Brazing
- SABIC Innovative Plastics LNP THERMOCOMP QC006I PA 6/10
- DuPont Bynel® 4109 Anhydride-Modified LLDPE Adhesive Resin
- 3M 225 Silver Weather-Resistant Masking Tape
- Asahi Glass Fluon® PA1015Z 15% Glass Fiber, PTFE Filled Compound
- Haynes 25 alloy, room temperature after 15% cold reduction
- Karina 802D18/441-CY-IS-AS-BZ Gray PVC Compound
Copyright © lookpolymers.com All Rights Reserved