Eurostar Starflam AF430B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam AF430B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam AFR430B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 5.5 % @Temperature 23.0 °C |
5.5 % @Temperature 73.4 °F |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.60 GPa | 957 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 247 °C | 477 °F | B/120; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 285 °C | 518 - 545 °F | |
| Melt Temperature | 270 - 285 °C | 518 - 545 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Parker Chomerics METALASTIC® Gasketing Wire Mesh EMI Gasket Selection Guide
- SABIC HP7022 Low Density Polyethylene for Injection Molding
- Kraton® G1641 H (SEBS) Linear Triblock Copolymer
- KaMin Hydragloss® 90 Clay
- Momentive Performance Materials IS808 Translucent Adhesive Sealant, General Purpose Paste
- SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11
- Lubrizol Estane® GP 58 DT Thermoplastic Polyurethane
- Aremco Aremco-Bond™ 2220 High Performance Epoxide
- Axiall 3014 Rigid PVC, Extrusion
- Solvay Specialty Polymers Diofan® A 036 Polyvinylidene Chloride (PVDC) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved