PTS PCA-3013 High Flow PC/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS PCA-3013 High Flow PC/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hours at 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa @Thickness 3.17 mm |
7500 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 150 % @Thickness 3.17 mm |
150 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 63.4 MPa @Thickness 3.17 mm |
9200 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.83 GPa @Thickness 3.17 mm |
265 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm @Thickness 3.17 mm |
13.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 252 - 274 °C | 485 - 525 °F | |
| Nozzle Temperature | 252 - 263 °C | 485 - 505 °F | |
| Melt Temperature | 249 - 271 °C | 480 - 520 °F | |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Back Pressure | 1.72 - 3.45 MPa | 250 - 500 psi | |
| Shot Size | 50 - 80 % | 50 - 80 % | |
| Screw Speed | 25 - 50 rpm | 25 - 50 rpm |
Users viewing this material also viewed the following:
- Hong Kun Group 2-Thiaxolidinethione; 2-Mercaptothiazoline Pharmaceutical Intermediate
- Manifattura Cattaneo PA 6.6 30% GF Nylon, Glass Filled
- Schott N-BAK4 Glass
- Silikony Polskie Polastosil M-33 Silicone Rubber
- Westlake EM182AA Low Density Polyethylene
- Total PPR 12232 Random Copolymer Polypropylene
- Eagle Brass 430 Ferritic Stainless Steel, 1/2 Hardened
- Elmer's Products Aron Alpha® 802 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- EMS-Grivory Grivory® HT2V-3X V0 black 9021 PA6T/66-GF30
- Chi Mei Polylac® PA-746 ABS - High Flow
Copyright © lookpolymers.com All Rights Reserved